Excellent Flexibility
Developed for EVA, RP and TPR materials.
Flexible & Specialty Material Ink Series
H103
H103 EVA/RP/TPR Ink
A single-component, low-odor aromatic solvent-based ink for elastic EVA, RP and TPR materials, providing flexibility, folding resistance and strong adhesion.
Excellent FlexibilityFolding ResistanceStrong AdhesionCrack Resistance
- Printing Method
- Screen Printing & Pad Printing
- Recommended Substrates
- EVA · RP · TPR · Elastic Plastic Materials
Printing MethodScreen Printing & Pad Printing
Ink TypeLow-odor aromatic solvent-based ink
Component TypeSingle-component
Drying MethodAir drying or low-temperature oven drying
Recommended SubstratesEVA · RP · TPR · Elastic plastics
Main ApplicationFlexible molded products
KEY PERFORMANCE
Performance built around the printed finish
Folding Resistance
No visible damage under the stated bending test.
Strong Adhesion
100/100 squares retained under the stated cross-cut test.
Crack Resistance
Maintains integrity after repeated deformation.
RECOMMENDED SUBSTRATES
Confirmed compatible materials
Performance depends on substrate, surface treatment, printing process and drying or curing conditions. Substrate testing is required before production.
TECHNICAL INFORMATION
Technical Information
Key reference data for product selection and printing evaluation.
- Product Type
- Low-odor aromatic solvent-based EVA/RP/TPR ink
- Printing Method
- Screen Printing & Pad Printing
- Recommended Substrates
- EVA, RP, TPR and other elastic plastic materials
- Component Type
- Single-component
- Surface Drying
- Hot air: 40–60°C (Recommended: 50°C)
- Full Drying
- Air dry for 24 hours, or oven cure at 80°C for 30 minutes
- Screen Mesh
- 100–150T
- Dry-Film Gloss
- ≥ 65 GU · 60° gloss meter
- Adhesion
- 100/100 squares retained · 1 mm × 1 mm, 100-grid cross-cut; 3M tape peel
- Folding Resistance
- No visible damage · Repeated bending test
View Additional Test Data
- Ink Fineness
- ≤ 12 μm · Grind gauge
- Flexibility
- No cracking or peeling · Folding test
- Abrasion Resistance
- No ink removal · Manual rubbing test
- Alcohol Resistance
- No visible change · Alcohol rubbing test
- Water Resistance
- No visible change · Tap-water immersion at 20°C for 96 h
- Heat Resistance
- No visible change · 80°C for 12 h
Test results are for reference only. Actual performance depends on substrate, surface treatment, printing process and drying or curing conditions.
Technical notes- Conduct a production trial on the actual substrate before mass printing.
- Remove dust, oil, release agents and other contaminants before printing.
- Drying and resistance may vary with substrate grade, ink-film thickness, temperature and ventilation.
PACKAGING OPTIONS
Packaging options
COMPLIANCE & DOCUMENTATION
Product documentation scope
The available documentation scope for this product includes the items shown below. Please identify the required color and destination market when requesting the applicable report.
- Product- and color-specific compliance documentation is available upon request.
- Confirm the required regulation, test method, color and target market before ordering.
TECHNICAL & CUSTOMIZATION SUPPORT
Support around the substrate, color and printing process
Match the required appearance using the confirmed substrate and reference.
Review adhesion, drying and resistance requirements together.
Evaluate the actual substrate, treatment and printing conditions.
Review leveling, edge definition, adhesion and drying issues.
WHY CHOOSE HONGSHENG
Focused support for industrial printing projects
Customized formulationSubstrate testing supportFlexible packaging supportConsistent product performance
Learn More About Hongsheng →